Abstract
Low band-gap conjugated polyelectrolytes (CPEs) can serve as efficient chromophores for use on photoelectrodes for dye-sensitized photoelectrochemical cells. Herein is reported a novel CPE based on poly(isoindigo-co-thiophene) with pendant sodium butylsulfonate groups (PiIT) and its use in construction of layer-by-layer (LbL) chromophore-catalyst assemblies with a Pt-based H+ reduction catalyst (PAA-Pt) for water reduction. A novel Stifle polymerization/postpolymerization ion-exchange strategy was used to convert an organic-soluble CPE to the water-soluble poly(isoindigo-co-thiophene). The anionic PiIT polyelectrolyte- and polyacrylate-stabilized Pt-nanoparticles (PAA-Pt) were codeposited with cationic poly(diallyldimethylammonium) chloride (PDDA) onto inverse opal (IO), nanostructured indium tin oxide film (nITO) (IO nITO) atop fluorine doped tin oxide (FTO), by using LbL self-assembly. To evaluate the performance of novel conjugated PiIT//PAA-Pt chromphore-catalyst assemblies, interassembly hole transfer was investigated by photocurrent density measurements on FTO//IO nITO electrodes. Enhanced cathodic photocurrent is observed for the polychromophore-catalyst assemblies, compared to electrodes modified with only PiIT, pointing toward photoinduced hole transfer from the excited PiIT to the IO nITO. Prolonged photoelectrolysis experiments reveal H-2 production with a Faradaic yield of approximately 45%. This work provides new routes to carry out visible-light-driven water reduction using photocathode assemblies based on low band-gap CPEs.